Ga2O3-based semiconductor element

ABSTRACT

A Ga2O3-based semiconductor element includes an undoped β-Ga2O3 single crystal film disposed on a surface of a β-Ga2O3 substrate, a source electrode and a drain electrode disposed on a same side of the undoped β-Ga2O3 single crystal film, a gate electrode disposed on the undoped β-Ga2O3 single crystal film between the source electrode and the drain electrode, and a region formed in the undoped β-Ga2O3 single crystal film under the source electrode and the drain electrode and including a controlled dopant concentration.

The present application is a Continuation Application of U.S. patent application Ser. No. 14/343,367, filed on Mar. 6, 2014, which is based on International Application No. PCT/JP2012/072897, filed on Sep. 7, 2012, which is based on Japanese Patent Application No. 2011-196435, filed on Sep. 8, 2011, the entire contents of which are incorporated herein by reference.

TECHNICAL FIELD

The invention relates to a Ga₂O₃-based semiconductor element.

BACKGROUND ART

A Ga₂O₃-based semiconductor element using a Ga₂O₃ crystal film formed on a sapphire substrate is known (see, e.g., NPLs 1 and 2).

CITATION LIST Non Patent Literature

[NPL 1]

-   K. Matsuzaki et al. Thin Solid Films 496, 2006, pp. 37-41.

[NPL 2]

-   K. Matsuzaki et al. Appl. Phys. Lett. 88, 092106, 2006.

SUMMARY OF INVENTION Technical Problem

However, since the crystal structure of Ga₂O₃ crystal is completely different from that of sapphire crystal, it is very difficult to heteroepitaxially grow a Ga₂O₃ crystal on a sapphire substrate. Thus, it is difficult to form a high-quality Ga₂O₃-based semiconductor element by using a Ga₂O₃ crystal film grown on a sapphire substrate.

It is an object of the invention to provide a high-quality Ga₂O₃-based semiconductor element.

Solution to Problem

According to one embodiment of the invention, a Ga₂O₃-based semiconductor element as defined in [1] to [6] below is provided so as to achieve the above object.

[1] A Ga₂O₃-based semiconductor element, comprising:

-   -   a β-Ga₂O₃ single crystal film that is formed on a β-Ga₂O₃         substrate directly or via an other layer;     -   a source electrode and a drain electrode that are formed on the         β-Ga₂O₃ single crystal film; and     -   a gate electrode that is formed on the β-Ga₂O₃ single crystal         film between the source electrode and the drain electrode.

[2] The Ga₂O₃-based semiconductor element according to [1], wherein the semiconductor element further comprises a Ga₂O₃-based MISFET, and

-   -   wherein the gate electrode is formed on the β-Ga₂O₃ single         crystal film via a gate insulating film.

[3] The Ga₂O₃-based semiconductor element according to [1] or [2], wherein the semiconductor element further comprises a source region and a drain region formed in the β-Ga₂O₃ single crystal film under the source electrode and the drain electrode, respectively.

[4] The Ga₂O₃-based semiconductor element according to [3], wherein the β-Ga₂O₃ single crystal film, the source region and the drain region are of an n-type, and

-   -   wherein the semiconductor element further comprises a p-type or         high-resistance body region formed in the β-Ga₂O₃ single crystal         film so as to surround the source region.

[5] The Ga₂O₃-based semiconductor element according to [1], wherein the semiconductor element further comprises a Ga₂O₃-based MESFET, and

-   -   wherein the gate electrode is formed directly on the β-Ga₂O₃         single crystal film.

[6] The Ga₂O₃-based semiconductor element according to [5], wherein the β-Ga₂O₃ single crystal film is of an n-type, and

-   -   wherein the semiconductor element further comprises an n-type         source region and an n-type drain region formed in the β-Ga₂O₃         single crystal film under the source electrode and the drain         electrode, respectively.

Advantageous Effects of Invention

According to an embodiment of the invention, a high-quality Ga₂O₃-based semiconductor element can be provided.

BRIEF DESCRIPTION OF DRAWINGS

FIG. 1 is a cross sectional view showing a Ga₂O₃-based MISFET in a first embodiment.

FIG. 2 is a schematic structural diagram illustrating a structure of an MBE system in the first embodiment.

FIG. 3A is a cross sectional view showing a high-resistance β-Ga₂O₃ substrate and an n-type β-Ga₂O₃ single crystal film in the first embodiment.

FIG. 3B is a cross sectional view showing a high-resistance β-Ga₂O₃ substrate and a n-type β-Ga₂O₃ single crystal film in the first embodiment.

FIG. 4 is a cross sectional view showing a Ga₂O₃-based MESFET in a second embodiment.

FIG. 5 is a cross sectional view showing a Ga₂O₃-based MISFET in a third embodiment.

FIG. 6 is a cross sectional view showing a Ga₂O₃-based MISFET in a fourth embodiment.

FIG. 7 is a cross sectional view showing a Ga₂O₃-based MISFET in a fifth embodiment.

FIG. 8 is a graph showing a relation between drain-to-source voltage and drain-to-source current in Example.

FIG. 9 is a graph showing a relation between gate-to-source voltage and drain-to-source current in Example.

FIG. 10 is a graph showing a relation between gate-to-drain voltage and gate-to-drain current in Example.

DESCRIPTION OF EMBODIMENTS

According to the present embodiment, it is possible to form a high-quality β-Ga₂O₃-based single crystal film by homoepitaxial growth and use of such a high-quality β-Ga₂O₃-based single crystal film allows a high-quality Ga₂O₃-based semiconductor element to be formed. Examples of embodiments thereof will be described in detail below.

First Embodiment

A Ga₂O₃-based MISFET (Metal Insulator Semiconductor Field Effect Transistor) as the high-quality Ga₂O₃-based semiconductor element will be described in the first embodiment.

(Structure of Ga₂O₃-Based MISFET)

FIG. 1 is a cross sectional view showing a Ga₂O₃-based MISFET 20 in the first embodiment. The Ga₂O₃-based MISFET 20 includes an n-type β-Ga₂O₃ single crystal film 3 forming on a high-resistance β-Ga₂O₃ substrate 2, a source electrode 22 and a drain electrode 23 which are formed on the n-type β-Ga₂O₃ single crystal film 3, a gate electrode 21 formed on the n-type β-Ga₂O₃ single crystal film 3 between the source electrode 22 and the drain electrode 23 via a gate insulating film 26, and a source region 24 and a drain region 25 which are formed in the n-type β-Ga₂O₃ single crystal film 3 respectively under the source electrode 22 and the drain electrode 23.

The high-resistance β-Ga₂O₃ substrate 2 is a β-Ga₂O₃ substrate of which resistance is increased by adding a p-type dopant such as Mg, H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Tl, Pb, N or P.

Plane orientation of the main surface of the high-resistance β-Ga₂O₃ substrate 2 is not specifically limited but a plane rotated by not less than 50° and not more than 90° with respect a (100) plane is preferable. In other words, in the high-resistance β-Ga₂O₃ substrate 2, an angle θ (0<θ≤90°) formed between the main surface and the (100) plane is preferably not less than 50°. Examples of the plane rotated by not less than 50° and not more than 90° with respect the (100) plane include a (010) plane, a (001) plane, a (−201) plane, a (101) plane and a (310) plane.

When the main surface of the high-resistance β-Ga₂O₃ substrate 2 is a plane rotated by not less than 50° and not more than 90° with respect the (100) plane, it is possible to effectively suppress re-evaporation of raw materials of the β-Ga₂O₃-based crystal from the high-resistance β-Ga₂O₃ substrate 2 at the time of epitaxially growing the β-Ga₂O₃-based crystal on the high-resistance β-Ga₂O₃ substrate 2. In detail, where a percentage of the re-evaporated raw material during growth of the β-Ga₂O₃-based crystal at a growth temperature of 500° C. is defined as 0%, the percentage of the re-evaporated raw material can be suppressed to not more than 40% when the main surface of the high-resistance β-Ga₂O₃ substrate 2 is a plane rotated by not less than 50° and not more than 90° with respect the (100) plane. It is thus possible to use not less than 60% of the supplied raw material to form the β-Ga₂O₃-based crystal, which is preferable from the viewpoint of growth rate and manufacturing cost of the β-Ga₂O₃-based crystal.

The β-Ga₂O₃ crystal has a monoclinic crystal structure and typically has lattice constants of a=12.23 Å, b=3.04 Å, c=5.80 Å, α=γ=90° and β=103.7°. In the β-Ga₂O₃ crystal, the (100) plane comes to coincide with the (310) plane when rotated by 52.5° around the c-axis and comes to coincide with the (010) plane when rotated by 90°. Meanwhile, the (100) plane comes to coincide with the (101) plane when rotated by 53.8° around the b-axis, comes to coincide with the (001) plane when rotated by 76.3° and comes to coincide with the (−201) plane when rotated by 53.8°.

Alternatively, the main surface of the high-resistance β-Ga₂O₃ substrate 2 may be a plane rotated at an angle of not more than 37.5° with respect to the (010) plane. In this case, it is possible to provide a steep interface between the high-resistance β-Ga₂O₃ substrate 2 and the n-type β-Ga₂O₃ single crystal film 3 and it is also possible to highly accurately control the thickness of the i-type β-Ga₂O₃ single crystal film 3.

The n-type β-Ga₂O₃ single crystal film 3 is an electrically conductive single crystal film formed on the high-resistance β-Ga₂O₃ substrate 2 by the below-described method. The n-type β-Ga₂O₃ single crystal film 3 includes an n-type dopant such as Sn, Ti, Zr, Hf, V, Nb, Ta, Mo, W, Ru, Rh, Ir, C, Si, Ge, Pb, Mn, As, Sb, Bi, F, Cl, Br and I. In addition, the thickness of the n-type β-Ga₂O₃ single crystal film 3 is, e.g., about 10 to 1000 nm.

Here, another film such as a non-doped β-Ga₂O₃ single crystal film may be formed between the high-resistance β-Ga₂O₃ substrate 2 and the n-type β-Ga₂O₃ single crystal film 3. In this case, the non-doped β-Ga₂O₃ single crystal film is formed on the high-resistance β-Ga₂O₃ substrate 2 by homoepitaxial growth and the n-type β-Ga₂O₃ single crystal film 3 is formed on the non-doped β-Ga₂O₃ single crystal film by homoepitaxial growth.

The gate electrode 21, the source electrode 22 and the drain electrode 23 are formed of, e.g., a metal such as Au, Al, Ti, Sn, Ge, In, Ni, Co, Pt, W, Mo, Cr, Cu and Pb, an alloy containing two or more of such metals, or a conductive compound such as ITO. In addition, the structure thereof may be a two-layer structure composed of two different metals, e.g., Al/Ti, Au/Ni or Au/Co.

The gate insulating film 26 is formed of an insulating material such as SiO₂, AlN, SiN, Al₂O₃ or β-(Al_(x)Ga_(1-x))₂O₃ (0≤x≤1). Of those, β-(Al_(x)Ga_(1-x))₂O₃ can be grown as a single crystal film on a β-Ga₂O₃ crystal and thus allows a good semiconductor/insulating film interface with less interface states to be formed, resulting in better gate characteristics than when using other insulating films.

The source region 24 and the drain region 25 are regions having a high n-type dopant concentration formed in the n-type β-Ga₂O₃ single crystal film 3 and are respectively connected to the source electrode 22 and the drain electrode 23. It should be noted that the source region 24 and the drain region 25 do not need to be provided in the Ga₂O₃-based MISFET 20.

The Ga₂O₃-based MISFET 20 is a normally-on transistor. The source electrode 22 is electrically connected to the drain electrode 23 via the n-type β-Ga₂O₃ single crystal film 3. Therefore, if a voltage is applied between the source electrode 22 and the drain electrode 23 without applying a voltage to the gate electrode 21, a current flows from the source electrode 22 to the drain electrode 23. On the other hand, when voltage is applied to the gate electrode 21, an inversion layer is formed in the n-type β-Ga₂O₃ single crystal film 3 in a region under the gate electrode 21 and a current does not flow from the source electrode 22 to the drain electrode 23 even when voltage is applied between the source electrode 22 and the drain electrode 23.

(Method of Manufacturing Ga₂O₃-Based MISFET)

The method of manufacturing the β-Ga₂O₃-based single crystal film is PLD (Pulsed Laser Deposition), CVD (Chemical Vapor Deposition), sputtering and MBE (Molecular Beam Epitaxy) etc. In the present embodiment, a thin film growth method using the MBE is employed. The MBE is a crystal growth method in which a single or compound solid is heated in an evaporation source called cell and vapor generated by heat is supplied as a molecular beam onto the surface of the substrate.

FIG. 2 is a structural diagram illustrating an example MBE system used for forming the β-Ga₂O₃-based single crystal film. The MBE system 1 is provided with a vacuum chamber 10, a substrate holder 11 supported in the vacuum chamber 10 to hold the high-resistance β-Ga₂O₃ substrate 2, heating devices 12 held on the substrate holder 11 to heat the high-resistance β-Ga₂O₃ substrate 2, plural cells 13 (13 a, 13 b) each provided for each atom or molecule constituting a thin film, heaters 14 (14 a, 14 b) for hearing the plural cells 13, a gas supply pipe 15 for supplying oxygen-based gas into the vacuum chamber 10, and a vacuum pump 16 for exhausting the air in the vacuum chamber 10. It is configured that the substrate holder 11 can be rotated by a non-illustrated motor via a shaft 110.

A Ga raw material of the β-Ga₂O₃-based single crystal film, such as Ga powder, is loaded in the first cell 13 a. The Ga powder desirably has a purity of not less than 6N. Powder of an n-type dopant raw material to be doped as a donor is loaded in the second cell 13 b. A shutter is provided at an opening of each of the first cell 13 a and the second cell 13 b.

The preliminarily-formed high-resistance β-Ga₂O₃ substrate 2 is attached to the substrate holder 11 and a β-Ga₂O₃ crystal is then homoepitaxially grown on the high-resistance β-Ga₂O₃ substrate 2 while adding an n-type dopant, thereby forming the n-type β-Ga₂O₃ single crystal film 3.

The high-resistance β-Ga₂O₃ substrate 2 is made by, e.g., the following procedure. Firstly, a semi-insulating β-Ga₂O₃ single crystal ingot doped with Mg is made by the EFG (edge-defined film-fed growth) method. It should be noted that an element to be doped is not limited to Mg. When substituting, e.g., Ga site, it is possible to use H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Ti or Pb. Meanwhile, it is possible to use N or P when substituting oxygen site. For doping Mg, MgO powder is mixed to raw material powder. Not less than 0.05 mol % of MgO is added to impart good insulation properties to the high-resistance β-Ga₂O₃ substrate 2. Alternatively, the semi-insulating β-Ga₂O₃ single crystal ingot may be made by the FZ (floating zone) method. The obtained ingot is sliced to a thickness of, e.g., about 1 mm so that the main surface has a desired plane orientation, thereby forming a substrate. Then, a grinding and polishing process is performed to a thickness of about 300 to 600 μm.

Next, the high-resistance β-Ga₂O₃ substrate 2 made by the above procedure is attached to the substrate holder 11 of the MBE system 1. Next, the vacuum pump 16 is activated to reduce atmospheric pressure in the vacuum chamber 10 to about 10⁻¹⁰ Torr. Then, the high-resistance β-Ga₂O₃ substrate 2 is heated by the heating devices 12. Here, radiation heat of heat source such as graphite heater of the heating device 12 is thermally transferred to the high-resistance β-Ga₂O₃ substrate 2 via the substrate holder 11 and the high-resistance β-Ga₂O₃ substrate 2 is thereby heated.

After the high-resistance β-Ga₂O₃ substrate 2 is heated to a predetermined temperature, oxygen-based gas is supplied into the vacuum chamber 10 through the gas supply pipe 15.

After a period of time required for stabilization of gas pressure in the vacuum chamber 10 (e.g., after 5 minutes) since the oxygen-based gas was supplied into the vacuum chamber 10, the first cell 13 a and the second cell 13 b are respectively heated by the first heater 14 a and the second heater 14 b while rotating the substrate holder 11 so that Ga and n-type dopant are evaporated and are radiated as molecular beam onto the surface of the high-resistance β-Ga₂O₃ substrate 2.

For example, the first cell 13 a is heated to 900° C. and beam-equivalent pressure (BEP) of Ga vapor is 1×10⁻⁴ Pa.

As such, the β-Ga₂O₃ crystal is homoepitaxially grown on the main surface of the high-resistance β-Ga₂O₃ substrate 2 while being doped with the n-type dopant such as Sn and the n-type β-Ga₂O₃ single crystal film 3 is thereby formed. Growth temperature of the β-Ga₂O₃ crystal is e.g., 700° C. It should be noted that as the n-type dopant other than Sn, it is possible to use Ti, Zr, Hf, V, Nb, Ta, Mo, W, Ru, Rh, Ir, C, Si, Ge, Pb, Mn, As, Sb and Bi, etc., for substituting Ga site and it is possible to use F, Cl, Br and I, etc., for substituting oxygen site.

Alternatively, the n-type β-Ga₂O₃ single crystal film 3 may be formed by the PLD (Pulsed Laser Deposition) or the CVD (Chemical Vapor Deposition) etc.

FIGS. 3A and 3B are cross sectional views showing the n-type β-Ga₂O₃ single crystal film 3 in the present embodiment. The n-type β-Ga₂O₃ single crystal film 3 is formed on a main surface 2 a of the high-resistance β-Ga₂O₃ substrate 2 by the MBE mentioned above.

FIG. 3A shows the n-type β-Ga₂O₃ single crystal film 3 which is formed by continuously adding the n-type dopant during homoepitaxial growth of the β-Ga₂O₃ crystal.

The donor concentration in the n-type β-Ga₂O₃ single crystal film 3 is, e.g., 1×10¹⁵ to 1×10¹⁹/cm³ and is especially preferably 1×10¹⁷ to 1×10¹⁸/cm³. This donor concentration can be controlled by temperature of the second cell 13 b during film formation.

FIG. 3B shows the n-type β-Ga₂O₃ single crystal film 3 which is formed by intermittently adding the n-type dopant at certain intervals during homoepitaxial growth of the β-Ga₂O₃ crystal. In this case, Sn is used as the n-type dopant.

In detail, Sn vapor is intermittently generated from the second cell 13 b by operating the shutter of the second cell 13 b, thereby intermittently adding Sn to the β-Ga₂O₃ single. It is preferable that Sn be intermittently added twice or more. In this case, electrical conductivity according to the added amount of Sn can be imparted to the n-type β-Ga₂O₃ single crystal film 3 without performing annealing treatment.

Due to intermittent Sn addition during the film formation, the n-type β-Ga₂O₃ single crystal film 3 in FIG. 3B has first layers 4 (4 a, 4 b, 4 c) grown during the period with no Sn addition and second layers 5 (5 a, 5 b, 5 c) grown during the period with Sn addition.

The Sn concentration in the second layer 5 can be controlled by temperature of the second cell 13 b during the film formation. The first layer 4, which ideally does not contain Sn, only contains a trace amount of Sn diffused from the second layer 5. Therefore, the Sn concentration in the first layer 4 is lower than that in the second layer 5. An average Sn concentration in the n-type β-Ga₂O₃ single crystal film 3 is, e.g., 1×10¹⁴ to 3×10¹⁸/cm³ and is especially preferably 1×10¹⁷ to 1×10¹⁸/cm³.

For example, the first layers 4 a, 4 b and 4 c are 3 to 20 nm in thickness and the second layers 5 a, 5 b and 5 c are 0.2 to 1 nm in thickness. If the thickness of the first layers 4 a, 4 b and 4 c is greater than 20 nm, the effect of providing the n-type may be reduced since intervals of the second layers 5 a, 5 b and 5 c are too large. On the other hand, if the thickness of the second layers 5 a, 5 b and 5 c is greater than 1 nm, the effect of intermittently providing the n-type may be reduced since the amount of Sn diffused from the second layers 5 a, 5 b and 5 c into the first layers 4 a, 4 b and 4 c is too large.

It should be noted that the lowermost layer of the n-type β-Ga₂O₃ single crystal film 3 (the layer in contact with the main surface 2 a of the high-resistance β-Ga₂O₃ substrate 2) may be either the first layer 4 or the second layer 5. In addition, the number of the first layers 4 and that of the second layers 5 are not limited.

After forming the n-type β-Ga₂O₃ single crystal film 3, the source region 24 and the drain region 25 are formed by ion-implanting the n-type dopant such as Sn into the n-type β-Ga₂O₃ single crystal film 3. It should be noted that the ion to be implanted is not limited to Sn and, when substituting, e.g., Ga site, it is possible to use Ti, Zr, Hf, V, Nb, Ta, Mo, W, Ru, Rh, Ir, C, Si, Ge, Pb, Mn, As, Sb or Bi. In addition, it is possible to use F, Cl, Br or I when substituting oxygen site. The implantation concentration is, e.g., not less than 1×10¹⁸/cm³ and not more than 5×10¹⁹ cm³. The implantation depth is not less than 30 nm. After implantation, the surface of the implanted region is etched about 10 nm by hydrofluoric acid. Sulfuric acid, nitric acid or hydrochloric acid may be used instead. After that, implantation damage is repaired by performing annealing treatment in a nitrogen atmosphere at not less than 800° C. for not less than 30 minutes. In case of performing the annealing treatment in an oxygen atmosphere, treatment temperature is not less than 800° C. and not more than 950° C. and treatment time is not less than 30 minutes.

It should be noted that the method of forming the source region 24 and the drain region 25 is not limited to ion implantation and thermal diffusion process may be used. In this case, after metal such as Sn is brought into contact with the n-type β-Ga₂O₃ single crystal film 3 in a region for the source region 24 and the drain region 25 to be formed, heat treatment is performed to diffuse a dopant such as Sn into the n-type β-Ga₂O₃ single crystal film 3. It should be noted that the source region 24 and the drain region 25 do not need to be formed.

After that, the gate insulating film 26, the source electrode 22, the drain electrode 23 and the gate electrode 21 are formed.

Second Embodiment

A Ga₂O₃-based MESFET (Metal Semiconductor Field Effect Transistor) as the Ga₂O₃-based semiconductor element will be described in the second embodiment.

(Structure of Ga₂O₃-Based MESFET)

FIG. 4 is a cross sectional view showing a Ga₂O₃-based MESFET 30 in the second embodiment. The Ga₂O₃-based MESFET 30 includes the n-type β-Ga₂O₃ single crystal film 3 formed on the high-resistance β-Ga₂O₃ substrate 2, a source electrode 32 and a drain electrode 33 which are formed on the n-type β-Ga₂O₃ single crystal film 3, a gate electrode 31 formed on the n-type β-Ga₂O₃ single crystal film 3 between the source electrode 32 and the drain electrode 33, and a source region 34 and a drain region 35 which are formed in the n-type β-Ga₂O₃ single crystal film 3 respectively under the source electrode 32 and the drain electrode 33.

The structure and the manufacturing method of the high-resistance β-Ga₂O₃ substrate 2 and those of the n-type β-Ga₂O₃ single crystal film 3 are the same as the first embodiment.

The gate electrode 31, the source electrode 32, the drain electrode 33, the source region 34 and the drain region 35 are formed in the same manner as the gate electrode 21, the source electrode 22, the drain electrode 23, the source region 24 and the drain region 25 in the first embodiment. It should be noted that the source region 34 and the drain region 35 do not need to be provided in the Ga₂O₃-based MESFET 30.

The source electrode 32 is electrically connected to the drain electrode 33 via the n-type β-Ga₂O₃ single crystal film 3. Meanwhile, a Schottky junction is formed at an interface between the gate electrode 31 and the n-type β-Ga₂O₃ single crystal film 3 and a depletion layer is thus formed in the n-type β-Ga₂O₃ single crystal film 3 under the gate electrode 31. The Ga₂O₃-based MESFET 30 functions as either a normally-off transistor or a normally-on transistor depending on the thickness of the depletion region.

Third Embodiment

FIG. 5 is a cross sectional view showing a Ga₂O₃-based MISFET 40 in the third embodiment. The Ga₂O₃-based MISFET 40 includes the n-type β-Ga₂O₃ single crystal film 3 formed on the high-resistance β-Ga₂O₃ substrate 2, a source electrode 42 and a drain electrode 43 which are formed on the n-type β-Ga₂O₃ single crystal film 3, a gate electrode 41 formed on the n-type β-Ga₂O₃ single crystal film 3 between the source electrode 42 and the drain electrode 43 via a gate insulating film 46, a source region 44 and a drain region 45 which are formed in the n-type β-Ga₂O₃ single crystal film 3 respectively under the source electrode 42 and the drain electrode 43, and a body region 47 surrounding the source region 44.

The structure and the manufacturing method of the high-resistance β-Ga₂O₃ substrate 2 and those of the n-type β-Ga₂O₃ single crystal film 3 are the same as the first embodiment.

The gate electrode 41, the source electrode 42, the drain electrode 43, the source region 44, the drain region 45 and the gate insulating film 46 are formed in the same manner as the gate electrode 21, the source electrode 22, the drain electrode 23, the source region 24, the drain region 25 and the gate insulating film 26 in the first embodiment. It should be noted that the source region 44 and the drain region 45 do not need to be provided in the Ga₂O₃-based MISFET 40.

The body region 47 includes a p-type dopant such as Mg, H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Tl, Pb, N or P. The body region 47 is a p-type region or a high resistance region which behaves like i-type due to charge compensation.

The body region 47 is formed by ion-implanting a p-type dopant such as Mg into the n-type β-Ga₂O₃ single crystal film 3. It should be noted that the ion to be implanted is not limited to Mg and, when substituting, e.g., Ga site, it is possible to use H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Tl or Pb. In addition, it is possible to use N or P when substituting oxygen site. After implanting the p-type dopant, damage caused by implantation is repaired by performing annealing treatment.

It should be noted that the method of forming the body region 47 is not limited to ion implantation and thermal diffusion process may be used. In this case, after a metal film such as Mg film is brought into contact with the n-type β-Ga₂O₃ single crystal film 3 in a region for the body region 47 to be formed, heat treatment is performed to diffuse a dopant such as Mg into the n-type β-Ga₂O₃ single crystal film 3.

The Ga₂O₃-based MISFET 40 functions as a normally-off transistor. In a state that voltage is not applied to the gate electrode 41, a current does not flow from the source electrode 42 to the drain electrode 43 due to the presence of the body region 47. When voltage of more than the threshold is applied to the gate electrode 41, a channel is formed in a region of the body region 47 under the gate electrode 41 and a current thus flows from the source electrode 42 to the drain electrode 43.

Fourth Embodiment

FIG. 6 is a cross sectional view showing a Ga₂O₃-based MISFET 50 in the fourth embodiment. The Ga₂O₃-based MISFET 50 includes an undoped β-Ga₂O₃ single crystal film 6 formed on the high-resistance β-Ga₂O₃ substrate 2, a source electrode 52 and a drain electrode 53 which are formed on the undoped β-Ga₂O₃ single crystal film 6, a gate electrode 51 formed on the undoped β-Ga₂O₃ single crystal film 6 between the source electrode 52 and the drain electrode 53 via a gate insulating film 56, and a source region 54 and a drain region 55 which are formed in the undoped β-Ga₂O₃ single crystal film 6 respectively under the source electrode 52 and the drain electrode 53.

The structure and the manufacturing method of the high-resistance β-Ga₂O₃ substrate 2 are the same as the first embodiment.

The gate electrode 51, the source electrode 52, the drain electrode 53, the source region 54, the drain region 55 and the gate insulating film 56 are formed in the same manner as the gate electrode 21, the source electrode 22, the drain electrode 23, the source region 24, the drain region 25 and the gate insulating film 26 in the first embodiment. It should be noted that the source region 54 and the drain region 55 do not need to be provided in the Ga₂O₃-based MISFET 50.

The undoped β-Ga₂O₃ single crystal film 6 is a high-resistance β-Ga₂O₃ single crystal film which does not include a dopant. Although there may be a case where conductivity thereof is low due to crystal defects, etc., electric resistance thereof is sufficiently high and a current never flows from the source electrode 52 to the drain electrode 53 unless voltage is applied to the gate electrode 51. The method of forming the undoped β-Ga₂O₃ single crystal film 6 is, e.g., based on the method of forming the n-type β-Ga₂O₃ single crystal film 3 in the first embodiment where the process of implanting the n-type dopant is eliminated.

The Ga₂O₃-based MISFET 50 functions as a normally-off transistor. When voltage of more than the threshold is applied to the gate electrode 51, a channel is formed in a region of the undoped β-Ga₂O₃ single crystal film 6 under the gate electrode 51 and a current thus flows from the source electrode 52 to the drain electrode 53.

Fifth Embodiment

FIG. 7 is a cross sectional view showing a Ga₂O₃-based MISFET 60 in the fifth embodiment. The Ga₂O₃-based MISFET 60 includes a p-type β-Ga₂O₃ single crystal film 7 formed on the high-resistance β-Ga₂O₃ substrate 2, a source electrode 62 and a drain electrode 63 which are formed on the p-type β-Ga₂O₃ single crystal film 7, a gate electrode 61 formed on the p-type β-Ga₂O₃ single crystal film 7 between the source electrode 62 and the drain electrode 63 via a gate insulating film 66, and a source region 64 and a drain region 65 which are formed in the p-type β-Ga₂O₃ single crystal film 7 respectively under the source electrode 62 and the drain electrode 63.

The structure and the manufacturing method of the high-resistance β-Ga₂O₃ substrate 2 are the same as the first embodiment.

The gate electrode 61, the source electrode 62, the drain electrode 63, the source region 64, the drain region 65 and the gate insulating film 66 are formed in the same manner as the gate electrode 21, the source electrode 22, the drain electrode 23, the source region 24, the drain region 25 and the gate insulating film 26 in the first embodiment.

The p-type β-Ga₂O₃ single crystal film 7 is a β-Ga₂O₃ single crystal film which includes a p-type dopant such as Mg, H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Ti, Pb, N or P. The method of forming the p-type β-Ga₂O₃ single crystal film 7 is, e.g., based on the method of forming the n-type β-Ga₂O₃ single crystal film 3 in the first embodiment where the process of implanting the n-type dopant is replaced with a process of implanting the p-type dopant.

The Ga₂O₃-based MISFET 60 functions as a normally-off transistor. When voltage of more than the threshold is applied to the gate electrode 61, a channel is formed in a region of the p-type β-Ga₂O₃ single crystal film 7 under the gate electrode 61 and a current thus flows from the source electrode 62 to the drain electrode 63.

Effects of the Embodiments

According to the present embodiment, it is possible to form high-quality β-Ga₂O₃ single crystal films by homoepitaxial growth and use of such β-Ga₂O₃ single crystal films allows high-quality Ga₂O₃-based MISFETs or Ga₂O₃-based MESFETs to be formed. In addition, these Ga₂O₃-based MISFETs and Ga₂O₃-based MESFETs have excellent performance since a high-quality β-Ga₂O₃ single crystal film is used as a channel layer.

It should be noted that the invention is not intended to be limited to the above-mentioned embodiments, and the various kinds of modifications can be implemented without departing from the gist of the invention. In addition, constituent elements of the above-mentioned embodiments can be arbitrarily combined without departing from the gist of the invention.

Examples

The Ga₂O₃-based MESFET 30 in the second embodiment was made and transistor characteristics thereof were evaluated.

(Manufacture of Ga₂O₃-Based MESFET)

Firstly, 0.25 mol % of MgO was mixed to Ga₂O₃ powder and a β-Ga₂O₃-based single crystal was then grown by the FZ method. Next, the high-resistance β-Ga₂O₃ substrate 2 was cut out of the grown β-Ga₂O₃-based single crystal so as to have a (010) plane as a main surface and was ground and polished to a thickness of about 350 μm.

Next, the high-resistance β-Ga₂O₃ substrate 2 was subjected to organic cleaning, acid cleaning and pure water cleaning and was then conveyed to the MBE system. Next, an n-type β-Ga₂O₃ single crystal was grown on the high-resistance β-Ga₂O₃ substrate 2 by the MBE to form the n-type β-Ga₂O₃ single crystal film 3. Here, temperature of the high-resistance β-Ga₂O₃ substrate 2 was set to 700° C., temperature of the first cell 13 a filled with Ga powder to 900° C. and temperature of the second cell 13 b filled with SnO₂ powder to 770° C. and the n-type β-Ga₂O₃ single crystal was grown for 30 minutes, thereby forming the n-type β-Ga₂O₃ single crystal film 3 having a thickness of 0.3 μm. The Sn concentration in the n-type β-Ga₂O₃ single crystal film 3 was about 8×10¹⁷/cm³.

After that, the source electrode 32 and the drain electrode 33 each made of Ti and the gate electrode 31 made of Pt were formed on the n-type β-Ga₂O₃ single crystal film 3. The source region 34 and the drain region 35 were not formed.

(Evaluation of Ga₂O₃-Based MESFET)

FIG. 8 is a graph showing a relation between drain-to-source voltage and drain-to-source current. In FIG. 8, the horizontal axis indicates voltage V_(DS) between the source electrode 32 and the drain electrode 33 and the vertical axis indicates current I_(DS) between the source electrode 32 and the drain electrode 33. Plural curved lines in the graph respectively shows values measured while changing voltage V_(GS) between the gate electrode 31 and the source electrode 32 from +2V to −24V by −2V.

As shown in FIG. 8, I_(DS) decreases with decreasing V_(GS) and it was conformed that the Ga₂O₃-based MESFET 30 operates normally.

FIG. 9 is a graph showing a relation between gate-to-source voltage and drain-to-source current. In FIG. 9, the horizontal axis indicates voltage V_(GS) between gate electrode 31 and the source electrode 32, the vertical axis on the left side indicates current I_(DS) between the drain electrode 33 and the source electrode 32 and the vertical axis on the right side indicates transconductance gm. A curved line on the left side in the graph shows I_(DS) and that on the right side shows gm. Voltage V_(DS) between the source electrode 32 and the drain electrode 33 was fixed to 40V.

As shown in FIG. 9, an on/off ratio (a ratio of I_(SD) when V_(GS)=0V to I_(SD) when V_(GS)=−20V) is as sufficiently large as four digits and it was conformed that the Ga₂O₃-based MESFET 30 has good transistor characteristics.

FIG. 10 is a graph showing a relation between gate-to-drain voltage and gate-to-drain current. In FIG. 10, the horizontal axis indicates voltage V_(GD) between the gate electrode 31 and the drain electrode 33 and the vertical axis indicates gate leakage current I_(GD) between the gate electrode 31 and the drain electrode 33.

As shown in FIG. 10, gate leakage current I_(GD) is in the order of μA in the region of V_(GD)=not more than −20V and it was conformed that the Ga₂O₃-based MESFET 30 has good transistor characteristics.

Although the embodiments and example of the invention have been described above, the invention according to claims is not to be limited to the above-mentioned embodiments and example. Further, it should be noted that all combinations of the features described in the embodiments and example are not necessary to solve the problem of the invention.

INDUSTRIAL APPLICABILITY

A high-quality Ga₂O₃-based semiconductor element is provided.

REFERENCE SIGNS LIST

-   1: MBE system -   2: high-resistance β-Ga₂O₃ substrate -   3: n-type β-Ga₂O₃ single crystal film -   6: undoped β-Ga₂O₃ single crystal film -   7: p-type β-Ga₂O₃ single crystal film -   20, 40, 50, 60: Ga₂O₃-based MESFET -   21, 31, 41, 51, 61: gate electrode -   22, 32, 42, 52, 62: source electrode -   23, 33, 43, 53, 63: drain electrode -   24, 34, 44, 54, 64: source region -   25, 35, 45, 55, 65: drain region -   26, 46, 56, 66: gate insulating film -   30: Ga₂O₃-based MESFET 

What is claimed is:
 1. A Ga₂O₃-based semiconductor element, comprising: an undoped β-Ga₂O₃ single crystal film disposed on a surface of a β-Ga₂O₃ substrate; a source electrode and a drain electrode disposed on a same side of the undoped β-Ga₂O₃ single crystal film; a gate electrode disposed on the undoped β-Ga₂O₃ single crystal film between the source electrode and the drain electrode via a gate insulating film; and a source region and a drain region formed in the undoped β-Ga₂O₃ single crystal film under the source electrode and the drain electrode, respectively, and including a controlled dopant concentration, wherein the β-Ga₂O₃ substrate comprises a semi-insulating β-Ga₂O₃ single crystal doped with an element selected from Mg, H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Tl, Pb, N, or P, wherein a channel is formed in a region of the undoped β-Ga₂O₃ single crystal film when a voltage of more than a threshold is applied to the gate electrode, and wherein a current only flow from the source electrode to the drain electrode through the undoped β-Ga₂O₃ single crystal film when the voltage is applied to the gate electrode.
 2. The Ga₂O₃-based semiconductor element according to claim 1, wherein the undoped β-Ga₂O₃ single crystal film is disposed on a main surface of a β-Ga₂O₃ substrate, the main surface being rotated from 50° to 90° with respect to a (100) plane.
 3. The Ga₂O₃-based semiconductor element according to claim 1, wherein the source region, and the drain region are n-type.
 4. The Ga₂O₃-based semiconductor element according to claim 1, wherein upper surfaces of the source region and the drain region are flush with an upper surface of the undoped β-Ga₂O₃ single crystal film.
 5. The Ga₂O₃-based semiconductor element according to claim 4, wherein the source electrode is disposed on the upper surface of the source region.
 6. The Ga₂O₃-based semiconductor element according to claim 5, wherein the gate electrode is disposed on the undoped β-Ga₂O₃ single crystal film via the gate insulating film disposed on a bottom surface of the gate electrode.
 7. The Ga₂O₃-based semiconductor element according to claim 6, wherein a bottom surface of the gate insulating film is disposed on the upper surfaces of the source region and the drain region.
 8. The Ga₂O₃-based semiconductor element according to claim 7, wherein the bottom surface of the gate insulating film is further disposed on the upper surface of the undoped β-Ga₂O₃ single crystal film.
 9. The Ga2O3-based semiconductor element according to claim 1, wherein the undoped β-Ga2O3 single crystal film is a high-resistance β-Ga2O3 single crystal film.
 10. The Ga₂O₃-based semiconductor element according to claim 1, wherein the Ga₂O₃-based semiconductor element includes a normally-off transistor.
 11. The Ga₂O₃-based semiconductor element according to claim 1, wherein the region of the undoped β-Ga₂O₃ single crystal film is disposed below the gate electrode.
 12. The Ga₂O₃-based semiconductor element according to claim 1, wherein the gate insulating film is spaced apart from the source electrode and the drain electrode.
 13. A Ga₂O₃-based semiconductor element, comprising: an undoped β-Ga₂O₃ single crystal film that is formed on a main surface of a β-Ga₂O₃ substrate; a source electrode and a drain electrode disposed on a same side of the β-Ga₂O₃ single crystal film; a gate electrode disposed on the undoped β-Ga₂O₃ single crystal film between the source electrode and the drain electrode via a gate insulating film; and a source region and a drain region formed in the undoped β-Ga₂O₃ single crystal film under the source electrode and the drain electrode, respectively, wherein the β-Ga₂O₃ substrate comprises a semi-insulaing β-Ga₂O₃ single crystal doped with an element selected from Mg, H, Li, Na, K, Rb, Cs, Fr, Be, Ca, Sr, Ba, Ra, Mn, Fe, Co, Ni, Pd, Cu, Ag, Au, Zn, Cd, Hg, Tl, Pb, N, or P, wherein a channel is formed in a region of the undoped β-Ga₂O₃ single crystal film when a voltage of more than a threshold is applied to the gate electrode, and wherein a current only flows from the source electrode to the drain electrode through the undoped β-Ga₂O₃ single crystal film when the voltage is applied to the gate electrode.
 14. The Ga₂O₃-based semiconductor element according to claim 13, wherein upper surfaces of the source region and the drain region are flush with an upper surface of the undoped β-Ga₂O₃ single crystal film.
 15. The Ga₂O₃-based semiconductor element according to claim 14, wherein the source electrode is disposed on the upper surfaces of the source region and the drain region.
 16. The Ga₂O₃-based semiconductor element according to claim 15, wherein the gate electrode is disposed on the undoped β-Ga₂O₃ single crystal film via the gate insulating film disposed on a bottom surface of the gate electrode.
 17. The Ga₂O₃-based semiconductor element according to claim 16, wherein a bottom surface of the gate insulating film is disposed on the upper surfaces of the source region and the drain region.
 18. The Ga₂O₃-based semiconductor element according to claim 17, wherein the bottom surface of the gate insulating film is further disposed on the upper surface of the undoped β-Ga₂O₃ single crystal film.
 19. The Ga₂O₃-based semiconductor element according to claim 13, wherein the main surface is rotated from 50° to 90° with respect to a (100) plane. 